Ingot ya Kotazi
- Vinthu vyakwamba: 99.99% vyapachanya-kutozga kwa quartz (SiO2)
- Fomu: Ingot yakukhora ya silinda/slab (yambura kupangika)
- Vigaŵa vya kufipirwa:<10ppm total metallic contaminants (Fe, Al, Ca, etc.)
- OH Vyamukati:<5ppm (low-hydroxyl grade available)
Kulongosora
Kupanga vinthu
Vinthu vyakwamba:
99.99% yapamwamba-kutozga kwakuphatikizgika kwa quartz (SiO2)
01
Fomu:
Ingot yakukhora ya silinda/slab (yambura kupangika)
02
Vigaŵa vya Kufipirwa:
<10ppm total metallic contaminants (Fe, Al, Ca, etc.)
03
OH Vyamukati:
<5ppm (low-hydroxyl grade available)
04
Katundu
|
Vinthu vyakuwoneka |
Vinthu vyakuzirwa |
|
Kutozgeka |
＞99.99% |
|
Unandi |
2.2g/sentimita3 |
|
Kuwonekera |
＞90% |
|
Kulimba kwa Mohs |
5.5--6.5 |
|
Malo ghakusintha |
1280 digiri |
|
Kufeweska Mfundo |
1780 digiri |
|
Nthowa yakuwotchera |
1250 digiri |
|
Kutentha kwapadera (20 - 350 digiri ) |
670J / kilogalamu. digiri |
|
Kuchitiska kwakutentha (20 digiri) |
1.4W/m digiri |
|
Kutentha kwakutentha (w/mk,1000 digiri) |
1.0-1.2 |
|
Indeksi ya kugaŵikana |
1.4585 |
|
Coefficient ya Kukura kwa Kutentha |
5.510 -7cm/sm. digiri |
|
Kutentha kwakutentha - |
1750--2050 digiri |
|
Kutentha kwa Uteŵeti kwa nyengo yifupi - |
1300 digiri |
|
Kutentha kwa nyengo yitali - |
1100 digiri |
|
Katundu wa Makemiko |
Vinthu vyakuzirwa |
|
Kulimbana na asidi |
Asidi wankhongono (kupaturako HF), alkali wankhongono, yankho la vyamoyo |
|
Kutentha kwakukulu Kulimbana na dzimbiri |
Wachita makola |
|
Vinthu vyambura kutowa vya visulo |
<5 ppm |
|
Katundu wa magesi |
Vinthu vyakuzirwa |
|
Kukana |
7107Ω.cm |
|
Nkhongono ya vyakutetezgera |
250~400kv/sentimita |
|
Kusintha kwa magesi |
3.7~3.9 |
|
Kuyamwa kwa magesi |
＜410-4 |
|
Kutaya kwa magesi |
＜110-4 |
|
Katundu wa Makina |
Vinthu vyakuzirwa |
|
Nkhongono zakufinyikizga |
1100MPa |
|
Nkhongono zakukhota |
MPa |
|
Nkhongono ya Tensile |
48MPa |
|
Chiŵerengero cha Poisson |
0.14~0.17 |
|
Modulus wa Young |
72000MPa |
|
Kudumula Modulus |
31000MPa |
Mapulogalamu
Semikondakitala:
- Vigaŵa vya chipinda cha CVD
- Ŵanthu awo ŵakupanga wafer
01
Kupanga vyakuwonera:
- Palije kanthu ka ma lensi, ma prism, mawindo
- Vigaŵa vya UV
02
Mafakitale:
- Magalasi ghakuwonera ghakutentha chomene
- Vigaŵa vyakupangika na plasma
03
Kafukufuku:
- Vinthu vyakuwonera vya laser
- Kupanga ndondomeko ya Vacuum
04
Uwemi
- Viheni vyapasi: Mabubble ghachoko waka / vyakusazgapo vs. quartz yakusungunuka
- Kukhaliska kwa Batch: Kuzomerezga kwakukhozga (± 0.5mm)
Ingot ya quartz yakuwonekerathu na ingot ya quartz yituŵa ya mkaka vikusangika
Mafumbo ghakufumbika
Q1: Kasi ingot ya quartz yikuyana wuli na silica wakupangika na ŵanthu?
A: Kulimbana kwa kutentha kwapamwamba kweni katundu wakuwoneka wakuyana waka. Silika wakupangika wali na UV yiwemi yakuthandazgika pasi pa 200nm.
Q2: Kasi ingot ya quartz yingagwiliskirika nchito mwaluŵiro kwambura kupanga makina?
A: Yayi – vikukhumbikwira kudumura / kupoliska kuti vigwiriskike nchito.
Q3: Kasi ni nyengo wuli iyo yingagwiliskirika nchito?
A: 1100 digiri yakulutilira (nyengo yifupi-kufika pa 1450 digiri ). Pamwamba pa 1200℃, pachokopachoko devitrification yikuchitika.
Q4: Kasi pali vyakufipirwa vya visulo?
A: Giredi yithu yakumanyikwa yili na<10ppm metals.
Tag yakutentha: ingot ya quartz, China ŵakupanga ingot ya quartz, ŵakupeleka, fakitare
Itumirani mafumbo
Iwe Ungatemwaso